| PRODUCTS |
FUNCTION |
ALLOY TYPE |
APPLICATION RATE |
REMARKS |
| CERAFLUX-5 |
Melting &Covering Flux |
All Aluminium alloys
Except high Mg.Alloys |
For Crucible Furnace: 0.5 - 1% of metal charge
Reverberatory Furnace : 125- 150 gm/ Sq. ft. of liquid pool area |
-- |
| CERAFLUX-11 |
Covering & Drossing Flux |
All Aluminium alloys
Except high Mg.Alloys |
For Crucible Furnace: 0.5 - 1% of metal charge
Reverberatory Furnace : 125- 150 gm/ Sq. ft. of liquid pool area |
-- |
| Ceraflux 40 |
Alkali removal flux |
High Magnesium Alloys |
0.25 kg to 1.5 kg per MT |
Magnesium Chloride base fluxes |
| CERAFLUX-66J |
Melting & Drossing Flux for Higher Recovery & less Dross) |
All aluminium alloys (Hypo-eutectic, Eutectic and Hyper-eutectic). |
For Crucible Furnace: 0.3 To 0.5% of metal charge
Reverberatory Furnace : 50gm To 75 gm Per Sq. ft. of liquid pool area |
The melting loss with this product is less compared to other fluxes |
| CERAFLUX-66 |
Sodium free covering / drossing flux. |
Aluminium Magnesium Alloys (Magnesium 1 – 4% ) and Hypereutectic Aluminium Silicon Alloys (Piston Alloys |
For Crucible Furnace : 0.5 - 1% of metal charge
For Reverberatory Furnace : 125- 150 gm/ Sq. ft. of |
Higher % recommended for loose and uncleaned scrap |
| CERAFLUX-PT |
Drossing cum Degassing of Flux
In Tablet form. |
All Aluminium alloys
Except high Mg.Alloys |
0.1 to 0.2 % of metal charge |
For plunging application |
| CERAFLUX-29 |
Modifying Flux |
Aluminium Silicon alloys hypoeutectic Range |
2 to 3 % of total metal quantity and a temperature of 740 – 750°C |
Use at High temp up to 800 °C |
| CERAFLUX-36 |
Modifying Flux |
Aluminium Silicon alloys eutectic Range |
3 to 4% of total metal quantity and a temperature of 700 – 710°C |
Use at High temp up to 740°C |
| CERAFLUX-88 |
Furnace cleaning |
All Aluminium alloys
|
Depending upon thickness of oxide buildup on furnace wall |
Apply on red hot surface of the furnace wall only. |
| CERAFLUX-56 |
To recover aluminium from hot dross or skimming |
All Aluminium alloys |
10 % for Hot Dross & 5 % for skimming. |
Apply on hot dross with metal dripping mechanism |
| CERAFLUX-57 |
Flux for Reclamming turnings and borings |
All Aluminium alloys |
1 to 5% depending upon the degree of dirtiness and oxidation of the scrap. |
-- |
| CERAFLUX-Zn |
Covering & Refining Flux for Zinc based Alloys. |
Zinc and Zinc base alloys |
0.5 to 1% on the liquid metal weight |
The recommended temperature range for the treatment of CERAFLUX- ZN is 430° - 460°C as at higher temperature, the rate of loss of zinc is more along with high fuming. |